Uses of Titanium and Water Jets and MISC

hross14 · 04-01-2008, 02:36 PM

So i have been thinking for quite some time now about how to lighten the load on the 4runner.

A lighter rig would mean less breakage and better mileage.

So in my demented little brain and spare time-i have been thinking about Axles, Driveshafts, Bumpers, and MISC parts. Why not Ti axles and the such? Stuff would cost more but it would but more could be used for the same weight.

I know if it broke then you really couldnt fix it in the field without proper sheilding--but couldnt you just turn up the gas some--delay the before and after shielding. Also, as an axle, Ti can bend/twist more without being affected structurally.

So we go back to cost$$. I have been looking at machine hours rates and water jets run about $100 and cut anything. If you copy the part and just tell them--this is what i want out of Ti it shouildnt cost much more than buying it from 4wheel parts supplier (i am saying copy the original part--not somebody elses design.

Bottom line--i am really interested in this metal for certain applications.

Think about it--drop a rigs weight by 500lbs--and you have that much less stress on your parts.

SO WHAT SAYS YOU--do i have any machinist/Ti welders out there that will chime in? Metallergists (Spell check)....

DeathCougar · 04-01-2008, 03:04 PM

First, you need to figure out the cost of titanium. There is a reason they dont use it in metal fab, its far too cost prohibitive.

hross14 · 04-01-2008, 03:08 PM

The costs are more--but if you do the design and yourself and take out the middle man--it get significantly cheaper.

for all intents and purposes let say you TIG the stuff yourself and buy machine/water jet hours.

You will see price come down quite a bit. I have priced rod and plate--and it is pricey--but doable.

mastacox · 04-01-2008, 03:08 PM

Second, you need to explicitly decide which parts you're interested in replacing. It will be very hard to gain a significant weight savings without replacing major parts such as major cross members, or even the frame itself.

Titanium probably isn't as good an option as aluminum, but aluminum might not really gain you much weight savings after you engineer the part to be just as strong or stonger.

olharleyman · 04-01-2008, 03:18 PM

I agree that the cost vs. weight saving is not going to be all that great and you will end up with a lighter weight 4runner worth a rediculious amount of money.
It is a good idea to try and find a way to lighten it up with stronger lighter parts maybe billet aluminum but that would still cost a assload after the milling and buying it.

Erich_870 · 04-01-2008, 03:23 PM

Quote:

Originally Posted by hross14

The costs are more--but if you do the design and yourself and take out the middle man--it get significantly cheaper.

for all intents and purposes let say you TIG the stuff yourself and buy machine/water jet hours.

You will see price come down quite a bit. I have priced rod and plate--and it is pricey--but doable.

What are the cost comparisons? Lets see some prices.

Also, the cost of cutting, machining or metal forming is still going to be very high. I agree that you will save money if you do the welding yourself, if you don't count your time as having any monitary value.

Erich

hross14 · 04-01-2008, 03:27 PM

[quote=hross14;50794537]

So in my demented little brain and spare time-i have been thinking about Axles, Driveshafts, Bumpers, and MISC parts. Why not Ti axles and the such? Stuff would cost more but it would but more could be used for the same weight.[quote]

These are the explicit parts-But let say for instance you made axle shafts--those are heavey--weight cut in half now---take my 115 lbs skid plate--cut that weight in half--lower links (that wont bend) cut that weight in half. Clockable T case member--cut that weight in half.....TJM at 105lbs--cut that in half, A-arms....drive shaft...brakets..... you get the picture

Axle housing--you can buy the tube already at the right size and then get to welding....

You dont have to think exactly when you are reducing the weight by 50%.

Problems i think about are--can it be splined like regular axles? If yes--i may be running Ti axles sometime in relatively near future.

mastacox · 04-01-2008, 03:39 PM

Quote:

Originally Posted by hross14

These are the explicit parts-But let say for instance you made axle shafts--those are heavey--weight cut in half now---take my 115 lbs skid plate--cut that weight in half--lower links (that wont bend) cut that weight in half. Clockable T case member--cut that weight in half.....TJM at 105lbs--cut that in half, A-arms....drive shaft...brakets..... you get the picture

Axle housing--you can buy the tube already at the right size and then get to welding....

You dont have to think exactly when you are reducing the weight by 50%.

Problems i think about are--can it be splined like regular axles? If yes--i may be running Ti axles sometime in relatively near future.

There are a lot of problems that you are not considering, not the least of which I doubt you can reduce the weight by 50% using budget minded titanium shopping. What alloy of Titanium are you looking at? Because just plain titanium doesn't have particurally good material properties...

You have to look at the material's stiffness as well as its yield strength to really decide how well it will handle as a replacement.

Sound like an etremely expensive operation to replace all of the little stuff on your 4Runner with Titanium... Axle shafts are small-time, not even worth the effort IMO. You might be on to something with your t-case x-member and front bumper, but it's doubtful you'll get a 50% weight reduction while retaining the same strength characteristics.

4bytruckin · 04-01-2008, 03:41 PM

titanium prices are going through the roof right now. we waterjet and laserjet all sorts of metals and alloys. titanium is a pain to work with. first it's not just the bar stock that gets costly . it's the additives to the water the can be expensive. just water doesn't work to well. welding with titanium isn't too easy . it warps pretty quick. so anything you make will have to be 1 piece . axle for instance will need to start out as a rod 7 inches thick and the shaped down so you can include the flange . all in all that will take a couple of hours and the cost for materials would be astronomical . kinda like a diamond toilet seat. looks nice and functional but can buy a normal one for $20. if your gonna spend money on axles just go dana 60's . for the price of one axle shaft you can get poison spider 9's front and rear. just my .02

hross14 · 04-02-2008, 07:50 AM

4By--these are the items i really wanted to hear about. Didnt know axles were machined as one part.

Would it be possible to weld a flange to the bar and then machine afterwards to get it straight again? Or does that significantly weaken the axle..i.e. it really needs to be one piece? Alot of the Ti i have purchased thus far has only been waste sheet metal so it was actually pretty cheap. but i havent done anything with it yet. was going to try and weld on it....

The Question from other--Assume that due diligence would be done prior to taking on this venture concerning type of alloy, yeild strength......THIS WOULD CERTAINLY BE A SEMI kinda novelty. I would rather have this stuffs than a Rolex..get my drift

More expensive than buy quite a bit yes--look on some ones face when they ask why your stuff never breaks, rusts or why you get great MPG--Priceless....IMHO

dirtoyboy · 04-02-2008, 08:33 AM

you do know titanium is sold by the gram/ounce right? probably not the most cost effective material.....

Increases in aerospace building and industrialization in China have been driving the price up recently

hross14 · 04-02-2008, 11:15 AM

Yeah i have noticed the price jump--the Chinesse are driving up everything......Metal is getting crazy--there was time there for a bit when structual steel was about the same price as alum.

These are the kind of things i waste my money on though....dont drive a new car, can afford my house...NO WIFE OR KIDS

Have two room mates and understand that it is cheaper to buy the tool and DIY on most projects.

I like to try something and see it fail then not to try it at all--

I wish we had more of these discussions here on the board.

My other idea(s) is to use UHMW for parts that hit rocks often--make mini skids out of them and when they need to be replaced--just cut a new piece.

Tylerars24 · 04-02-2008, 08:52 PM

titanium is harder then aluminum but significantly softer than steel

titanium splines would have to be huge to handle the same torques as their steel counterparts.

that rules out: transmission internals, driveshafts, axles, what else?

cost is the next factor.

tc · 04-02-2008, 09:22 PM

OK - let's stop with the speculation and misinformation now.

I am a metallurgist with about 10 yrs of working for the nation's #1 and #2 manufacturers of titanium (www.timet.com www.allvac.com)

The graph above is modulus of elasticity, not strength or hardness. Think of modulus as "stiffness". Titanium is VERY springy stuff.

Strength-to-weight of titanium alloys is better than most anything out there. As a matter of fact, for our applications, it may indeed be the ultimate material if other factors were the same. The strength of alloyed titanium is higher than low alloy steel, and the density is lower. Weight savings of 70% are typical for properly designed parts.

Unfortunately, the other factors aren't the same - not even close:

FIRST
You may be finding scraps for a reaonable price, but just a forged billet goes for $10/pound - we had some thinner sheet that was over $100/lb! Tubing is even higher due to the fabrication issues. This project is going to be seriously spendy!

SECOND
Welding titanium is more difficult than you can imagine. It NEEDS to be done in a vacuum or a totally inert atmosphere. Titanium is VERY reactive, especially with oxygen and nitrogen at elevated temperatures. If there is even 1 molecule of O2 or N2, your weld is crap.

THIRD
Machining of titanium is not technically any more difficult than steel, nickel alloys, or aluminum, but it is a helluva lot less forgiving. Your feeds and speeds have to be dead on or you will never hold any kind of tolerance due to the low modulus. The chips are flammable (think magnesium, only worse) so care has to be taken in shops where they do it - Joe Machinist on the corner has no business trying to do titanium.
(To illustrate how reactive titanium is, if we had a cooling water leak in our melting furnaces, the shop had to be evacuated IMMEDIATELY as the Ti would steal the O atom off the water molecule - you would get a steam explosion, then a hydrogen explosion)

SO, titanium could maybe make sense for simple sheet metal parts that could be fabricated by shearing and braking, like skid plates, but for anything truly fabricated, the costs rise so sharply that it would be insane.

hross14 · 04-03-2008, 07:23 AM

And now I know--and knowing is half the battle

I have read alot about Ti, but getting first hand expereince is certainly more useful...

I knew Ti was reactive--just not that reactive. Was thinking more along the lines that when you welded it (using Argon right) you have to have long shielding times before and after the start of a weld.

Like i have said before...Like seeing if something can be done and then being told it cant versus just not trying new stuff at all.

So stamped parts and sheet metal stuffs is what we are left with then.

If i may ask--How Do y'all weld the stuff? It can be tig welded right as long as you have the right inert gas? What is used as a cooling fluid when machining--oil?

Thanks for the info

Erich_870 · 04-03-2008, 11:09 AM

Quote:

Originally Posted by tc

OK - let's stop with the speculation and misinformation now.

I am a metallurgist with about 10 yrs of working for the nation's #1 and #2 manufacturers of titanium (www.timet.com www.allvac.com)

The graph above is modulus of elasticity, not strength or hardness. Think of modulus as "stiffness". Titanium is VERY springy stuff.

Strength-to-weight of titanium alloys is better than most anything out there. As a matter of fact, for our applications, it may indeed be the ultimate material if other factors were the same. The strength of alloyed titanium is higher than low alloy steel, and the density is lower. Weight savings of 70% are typical for properly designed parts.

Unfortunately, the other factors aren't the same - not even close:

FIRST
You may be finding scraps for a reaonable price, but just a forged billet goes for $10/pound - we had some thinner sheet that was over $100/lb! Tubing is even higher due to the fabrication issues. This project is going to be seriously spendy!

SECOND
Welding titanium is more difficult than you can imagine. It NEEDS to be done in a vacuum or a totally inert atmosphere. Titanium is VERY reactive, especially with oxygen and nitrogen at elevated temperatures. If there is even 1 molecule of O2 or N2, your weld is crap.

THIRD
Machining of titanium is not technically any more difficult than steel, nickel alloys, or aluminum, but it is a helluva lot less forgiving. Your feeds and speeds have to be dead on or you will never hold any kind of tolerance due to the low modulus. The chips are flammable (think magnesium, only worse) so care has to be taken in shops where they do it - Joe Machinist on the corner has no business trying to do titanium.
(To illustrate how reactive titanium is, if we had a cooling water leak in our melting furnaces, the shop had to be evacuated IMMEDIATELY as the Ti would steal the O atom off the water molecule - you would get a steam explosion, then a hydrogen explosion)

SO, titanium could maybe make sense for simple sheet metal parts that could be fabricated by shearing and braking, like skid plates, but for anything truly fabricated, the costs rise so sharply that it would be insane.

Talk about a buzz kill!!

Thanks for sharing such good info! I've always wondered and it's great to see Yotatech's diverse and well educated membership step up with top industry knowledge.

Erich

tc · 04-03-2008, 11:47 AM

Can be TIG or MIG.

Standard cutting oil fluids are used, generally high lubricity versions, with TONS of flow as machining Ti generates quite a bit of heat.

http://www.timet.com/pdfs/ti-handbook.pdf

hross14 · 04-03-2008, 12:19 PM

Thanks for that read TC--i think i just might try some Ti projects and see what happens. That pamphlet had some of the best info i have read as of yet. to the point--common sense and the little things you need to know about doing it.

I think my first project will probably be a skid plate and the T-case mount so i can flatten my belly-

you dont have a small time supplier you recommend do ya?

04-01-2008, 02:36 PM	#1 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	Uses of Titanium and Water Jets and MISC So i have been thinking for quite some time now about how to lighten the load on the 4runner. A lighter rig would mean less breakage and better mileage. So in my demented little brain and spare time-i have been thinking about Axles, Driveshafts, Bumpers, and MISC parts. Why not Ti axles and the such? Stuff would cost more but it would but more could be used for the same weight. I know if it broke then you really couldnt fix it in the field without proper sheilding--but couldnt you just turn up the gas some--delay the before and after shielding. Also, as an axle, Ti can bend/twist more without being affected structurally. So we go back to cost$$. I have been looking at machine hours rates and water jets run about $100 and cut anything. If you copy the part and just tell them--this is what i want out of Ti it shouildnt cost much more than buying it from 4wheel parts supplier (i am saying copy the original part--not somebody elses design. Bottom line--i am really interested in this metal for certain applications. Think about it--drop a rigs weight by 500lbs--and you have that much less stress on your parts. SO WHAT SAYS YOU--do i have any machinist/Ti welders out there that will chime in? Metallergists (Spell check).... __________________ Yes, I said "country." America really is a nation, but you couldn't convince those who lead the Democratic and Republican Parties of that. Both parties now see America as nothing more than an economy, a marketplace, and not a sovereign nation. They don't see you and me as citizens of this great nation; they see us as units of labor, consumers and taxpayers. Yes, I am here to collect my 238$ worth of stock from AIG. "What do you mean a free market economy doesnt apply to the rich?"

04-01-2008, 03:08 PM	#3 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	The costs are more--but if you do the design and yourself and take out the middle man--it get significantly cheaper. for all intents and purposes let say you TIG the stuff yourself and buy machine/water jet hours. You will see price come down quite a bit. I have priced rod and plate--and it is pricey--but doable. __________________ Yes, I said "country." America really is a nation, but you couldn't convince those who lead the Democratic and Republican Parties of that. Both parties now see America as nothing more than an economy, a marketplace, and not a sovereign nation. They don't see you and me as citizens of this great nation; they see us as units of labor, consumers and taxpayers. Yes, I am here to collect my 238$ worth of stock from AIG. "What do you mean a free market economy doesnt apply to the rich?"

04-01-2008, 03:08 PM	#4 (permalink)
mastacox Contributing Member Join Date: Dec 2003 Location: Los Alamos, NM Posts: 2,453	Second, you need to explicitly decide which parts you're interested in replacing. It will be very hard to gain a significant weight savings without replacing major parts such as major cross members, or even the frame itself. Titanium probably isn't as good an option as aluminum, but aluminum might not really gain you much weight savings after you engineer the part to be just as strong or stonger. __________________ Brian 1998 4Runner SR5

04-01-2008, 03:18 PM	#5 (permalink)
olharleyman Contributing Member Join Date: Dec 2006 Location: maryland Posts: 1,838	I agree that the cost vs. weight saving is not going to be all that great and you will end up with a lighter weight 4runner worth a rediculious amount of money. It is a good idea to try and find a way to lighten it up with stronger lighter parts maybe billet aluminum but that would still cost a assload after the milling and buying it. __________________ 1990 4 runner 5 Speed Pro Comp Stage II 4" Lift 6" coils rear Aussie Locker front 5.29's Front And Rear 35 x 12.5 x 15 MT's Micky Thompson Classic II Wheels Super Charged 3.4 on the way 1993 SAS 4runner 22re 5 speed 4" front 5"rear 5.29's 35 x 12.5 BFG KM'S Dick cepek DC 1's 1955 Harley Davidson Springer Stock 1955 Hardtail Frame 4 Speed Kick Start Only Streached 5.5 gal. tanks 16" Ape Hangers 3" open primary 1998 Harley Custom Dresser 107 rwhp 139 ft.lbs.trq.

04-01-2008, 03:27 PM	#7 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	[quote=hross14;50794537] So in my demented little brain and spare time-i have been thinking about Axles, Driveshafts, Bumpers, and MISC parts. Why not Ti axles and the such? Stuff would cost more but it would but more could be used for the same weight.[quote] These are the explicit parts-But let say for instance you made axle shafts--those are heavey--weight cut in half now---take my 115 lbs skid plate--cut that weight in half--lower links (that wont bend) cut that weight in half. Clockable T case member--cut that weight in half.....TJM at 105lbs--cut that in half, A-arms....drive shaft...brakets..... you get the picture Axle housing--you can buy the tube already at the right size and then get to welding.... You dont have to think exactly when you are reducing the weight by 50%. Problems i think about are--can it be splined like regular axles? If yes--i may be running Ti axles sometime in relatively near future. __________________ Yes, I said "country." America really is a nation, but you couldn't convince those who lead the Democratic and Republican Parties of that. Both parties now see America as nothing more than an economy, a marketplace, and not a sovereign nation. They don't see you and me as citizens of this great nation; they see us as units of labor, consumers and taxpayers. Yes, I am here to collect my 238$ worth of stock from AIG. "What do you mean a free market economy doesnt apply to the rich?"

04-01-2008, 03:41 PM	#9 (permalink)
4bytruckin Registered User Join Date: Jul 2006 Posts: 168	titanium prices are going through the roof right now. we waterjet and laserjet all sorts of metals and alloys. titanium is a pain to work with. first it's not just the bar stock that gets costly . it's the additives to the water the can be expensive. just water doesn't work to well. welding with titanium isn't too easy . it warps pretty quick. so anything you make will have to be 1 piece . axle for instance will need to start out as a rod 7 inches thick and the shaped down so you can include the flange . all in all that will take a couple of hours and the cost for materials would be astronomical . kinda like a diamond toilet seat. looks nice and functional but can buy a normal one for $20. if your gonna spend money on axles just go dana 60's . for the price of one axle shaft you can get poison spider 9's front and rear. just my .02

04-02-2008, 07:50 AM	#10 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	4By--these are the items i really wanted to hear about. Didnt know axles were machined as one part. Would it be possible to weld a flange to the bar and then machine afterwards to get it straight again? Or does that significantly weaken the axle..i.e. it really needs to be one piece? Alot of the Ti i have purchased thus far has only been waste sheet metal so it was actually pretty cheap. but i havent done anything with it yet. was going to try and weld on it.... The Question from other--Assume that due diligence would be done prior to taking on this venture concerning type of alloy, yeild strength......THIS WOULD CERTAINLY BE A SEMI kinda novelty. I would rather have this stuffs than a Rolex..get my drift More expensive than buy quite a bit yes--look on some ones face when they ask why your stuff never breaks, rusts or why you get great MPG--Priceless....IMHO __________________ Yes, I said "country." America really is a nation, but you couldn't convince those who lead the Democratic and Republican Parties of that. Both parties now see America as nothing more than an economy, a marketplace, and not a sovereign nation. They don't see you and me as citizens of this great nation; they see us as units of labor, consumers and taxpayers. Yes, I am here to collect my 238$ worth of stock from AIG. "What do you mean a free market economy doesnt apply to the rich?"

04-02-2008, 11:15 AM	#12 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	Yeah i have noticed the price jump--the Chinesse are driving up everything......Metal is getting crazy--there was time there for a bit when structual steel was about the same price as alum. These are the kind of things i waste my money on though....dont drive a new car, can afford my house...NO WIFE OR KIDS Have two room mates and understand that it is cheaper to buy the tool and DIY on most projects. I like to try something and see it fail then not to try it at all-- I wish we had more of these discussions here on the board. My other idea(s) is to use UHMW for parts that hit rocks often--make mini skids out of them and when they need to be replaced--just cut a new piece. __________________ Yes, I said "country." America really is a nation, but you couldn't convince those who lead the Democratic and Republican Parties of that. Both parties now see America as nothing more than an economy, a marketplace, and not a sovereign nation. They don't see you and me as citizens of this great nation; they see us as units of labor, consumers and taxpayers. Yes, I am here to collect my 238$ worth of stock from AIG. "What do you mean a free market economy doesnt apply to the rich?"

04-02-2008, 08:52 PM	#13 (permalink)
Tylerars24 Registered User Join Date: Aug 2007 Location: On top of your wife. Posts: 127	titanium is harder then aluminum but significantly softer than steel titanium splines would have to be huge to handle the same torques as their steel counterparts. that rules out: transmission internals, driveshafts, axles, what else? cost is the next factor. __________________ pickup, sas, 63s, custom high-steer

04-02-2008, 09:22 PM	#14 (permalink)
tc Contributing Member Join Date: Nov 2005 Location: Longmont, CO Posts: 6,881	OK - let's stop with the speculation and misinformation now. I am a metallurgist with about 10 yrs of working for the nation's #1 and #2 manufacturers of titanium (www.timet.com www.allvac.com) The graph above is modulus of elasticity, not strength or hardness. Think of modulus as "stiffness". Titanium is VERY springy stuff. Strength-to-weight of titanium alloys is better than most anything out there. As a matter of fact, for our applications, it may indeed be the ultimate material if other factors were the same. The strength of alloyed titanium is higher than low alloy steel, and the density is lower. Weight savings of 70% are typical for properly designed parts. Unfortunately, the other factors aren't the same - not even close: FIRST You may be finding scraps for a reaonable price, but just a forged billet goes for $10/pound - we had some thinner sheet that was over $100/lb! Tubing is even higher due to the fabrication issues. This project is going to be seriously spendy! SECOND Welding titanium is more difficult than you can imagine. It NEEDS to be done in a vacuum or a totally inert atmosphere. Titanium is VERY reactive, especially with oxygen and nitrogen at elevated temperatures. If there is even 1 molecule of O2 or N2, your weld is crap. THIRD Machining of titanium is not technically any more difficult than steel, nickel alloys, or aluminum, but it is a helluva lot less forgiving. Your feeds and speeds have to be dead on or you will never hold any kind of tolerance due to the low modulus. The chips are flammable (think magnesium, only worse) so care has to be taken in shops where they do it - Joe Machinist on the corner has no business trying to do titanium. (To illustrate how reactive titanium is, if we had a cooling water leak in our melting furnaces, the shop had to be evacuated IMMEDIATELY as the Ti would steal the O atom off the water molecule - you would get a steam explosion, then a hydrogen explosion) SO, titanium could maybe make sense for simple sheet metal parts that could be fabricated by shearing and braking, like skid plates, but for anything truly fabricated, the costs rise so sharply that it would be insane. __________________ Check out www.coTTORA.org to hook up with great Toyota 'wheelin' folks! Current - 93 4Runner: 3VZ 33"x10.50" no lift ARB F/R 96 Impala SS: My own personal cop car Previous - 89 2WD Pickup 22R, Fabtech "Ivan Dan" lift, 31x10.50, IASCA World Finals 4th Place Stop with the mods and get on the trail! Pix at www.4wheelingoh.shutterfly.com/action

04-03-2008, 07:23 AM	#15 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	And now I know--and knowing is half the battle I have read alot about Ti, but getting first hand expereince is certainly more useful... I knew Ti was reactive--just not that reactive. Was thinking more along the lines that when you welded it (using Argon right) you have to have long shielding times before and after the start of a weld. Like i have said before...Like seeing if something can be done and then being told it cant versus just not trying new stuff at all. So stamped parts and sheet metal stuffs is what we are left with then. If i may ask--How Do y'all weld the stuff? It can be tig welded right as long as you have the right inert gas? What is used as a cooling fluid when machining--oil? Thanks for the info __________________ Yes, I said "country." America really is a nation, but you couldn't convince those who lead the Democratic and Republican Parties of that. Both parties now see America as nothing more than an economy, a marketplace, and not a sovereign nation. They don't see you and me as citizens of this great nation; they see us as units of labor, consumers and taxpayers. Yes, I am here to collect my 238$ worth of stock from AIG. "What do you mean a free market economy doesnt apply to the rich?"

04-03-2008, 11:47 AM	#17 (permalink)
tc Contributing Member Join Date: Nov 2005 Location: Longmont, CO Posts: 6,881	Can be TIG or MIG. Standard cutting oil fluids are used, generally high lubricity versions, with TONS of flow as machining Ti generates quite a bit of heat. http://www.timet.com/pdfs/ti-handbook.pdf __________________ Check out www.coTTORA.org to hook up with great Toyota 'wheelin' folks! Current - 93 4Runner: 3VZ 33"x10.50" no lift ARB F/R 96 Impala SS: My own personal cop car Previous - 89 2WD Pickup 22R, Fabtech "Ivan Dan" lift, 31x10.50, IASCA World Finals 4th Place Stop with the mods and get on the trail! Pix at www.4wheelingoh.shutterfly.com/action

04-03-2008, 12:19 PM	#18 (permalink)
hross14 Registered User Join Date: Feb 2006 Location: Austin Texas Posts: 811	Thanks for that read TC--i think i just might try some Ti projects and see what happens. That pamphlet had some of the best info i have read as of yet. to the point--common sense and the little things you need to know about doing it. I think my first project will probably be a skid plate and the T-case mount so i can flatten my belly- you dont have a small time supplier you recommend do ya?